Mungo 4200 crack pouring epoxy resin crack pouring Epoxy concrete crack pouring reinforcing material (DPOH-420090AB)
Mungo 4200 crack pouring epoxy resin crack pouring Epoxy concrete crack pouring reinforcing material (DPOH-420090AB)
Couldn't load pickup availability
The structural system of the building loses part of its seismic resistance due to damage from earthquake forces. If the section is not reinforced and repaired, stress concentration will form on the original fractures during another earthquake, which will intensify the damage and reduce safety.
Mungo 4200 crack-injecting epoxy resin (Epoxy) is a low-viscosity, two-liquid, room-temperature curing epoxy resin-infused repair material that has been widely used for repairing and reinforcing cracks in concrete structures. This injection resin does not contain solvents, has little shrinkage after hardening, and has excellent adhesion to various structures. With the mechanical infusion method (high-pressure infusion) or the syringe injection method (low-pressure infusion), fine cracks in the structure can be repaired. Give full play to the effect of reinforcement, restore the integrity of the structure, and achieve the purpose of integration.
Crack pouring epoxy resin is mostly used for low-pressure crack pouring and reinforcement. Its purpose is to block the infiltration of air and moisture, prevent steel bars from rusting, and neutralize concrete. And the separated concrete surfaces on both sides of the crack are bonded and compounded, and the loose concrete is re-bonded to achieve a strengthening effect.
feature of product:
- Crack infusion epoxy resin (Epoxy crack infusion artificial resin, crack infusion artificial resin, crack infusion resin glue)
- Crack-injecting epoxy resin (Epoxy) is a low-viscosity, two-liquid type, room-temperature hardening epoxy resin-injected repair material that has been widely used for repairing and reinforcing cracks in concrete structures.
- It is used for pouring and reinforcing low-pressure cracks. Its purpose is to block the infiltration of air and moisture, prevent steel bars from rusting, and neutralize concrete.
- The separated concrete surfaces on both sides of the crack are bonded and compounded, and the loose concrete is re-bonded to achieve a strengthening effect.
Low pressure perfusion features:
- Using low pressure and low speed continuous injection, every detail of the crack can be reliably injected.
- The amount of injection can be visually checked and epoxy resin can be replenished at any time.
- The pressure can be flexibly adjusted.
Product Usage :
Structural elements such as reinforced concrete buildings, main towers, bridge piers, abutments, tunnels, harbors, wharves, breakwaters, dams, sand dams, short bridges, spacer beams, main beams, etc., such as building apartments, etc., have cracks with a width of more than 0.3mm. For structural cracks, epoxy resin is injected under pressure to fill the cracks to repair damaged structural elements such as beams, columns, boards and walls, and to prevent moisture from penetrating and causing corrosion of steel bars.
Product characteristics :
A (main ingredient) | B(hardener) | |
Exterior | colorless liquid | Light brown transparent liquid |
viscosity | 500±200 | 300±100 |
Mixing ratio (weight) | 2 | 1 |
proportion | 1.05 | |
Available time | 90 minutes | |
Initial hardening time | 4-6 hours |
※Set the temperature at 25 degrees C
Physical data:
Test items | Test Methods | unit | Specification Value |
---|---|---|---|
Compression yield strength | ASTM D695 | Kg/cm 2 | >500 |
Bending strength | ASTM D790 | Kg/cm 2 | >400 |
tensile strength | ASTM D638 | Kg/cm 2 | >300 |
Bonding strength | ASTM C882/C882M | Kg/cm 2 | >100 |